The Nickel Cadmium battery, NiCD or NiCad is a form of rechargeable battery that has been used for many years - it was easy to use, but now poses problems to dispose because of issues with cadmium it contains.

    Home   » Electronic components » this page

Nickel Cadmium Battery includes:   NiCad     NiCad charging     NiCad memory effect    

Battery Technology Includes:   Battery technology overview     Battery definitions & terms     Zinc carbon     Alkaline     Zinc air cells     NiCad     NiMH     Li-ion     Lead acid    

The Nickel Cadmium, NiCd or NiCad battery was the first type of rechargeable cell that could be used for portable electronics equipment.

Although the Lead Acid battery had been available for many years, it was mainly used for automotive batteries. Th NiCd could easily be used as a direct replacement for many standard primary batteries and its use quickly caught on.

NiCd cells are less widely used these days because of the cadmium they contain. The cells or batteries need to be disposed of via the correct routes as the cadmium is harmful and can ultimately leach out into the ground if found in landfill.

Currently few NiCd batteries can be bought, but did fill a gap in the market that no other battery of the time could meet. Occasionally old NiCd batteries can still be found in stocks or possibly even in use.

NiCd vs NiCad

Often the abbreviation NiCd is used to describe nickel cadmium cells. The abbreviation NiCad is also widely used.

The abbreviation NiCad is a registered trademark of SAFT Corporation - a manufacturer of batteries and power sources. Therefore the abbreviation NiCad should not be used to refer generically to nickel-cadmium batteries, only to those manufactured by SAFT.

The abbreviation NiCd is therefore the recognized generic abbreviation for the generic nickel cadmium cells and batteries.

NiCd basics

NiCd or NiCad cells are able to provide an almost direct replacements for zinc carbon or alkaline primary batteries. They generally are able to retain less charge than these cells, but have the obvious advantage that they are able to be re-charged. This means that although the initial purchase cost is higher than the equivalent primary cells, costs can be saved after a few charge / discharge cycles.

The nominal cell voltage for a NiCd / Nickel cadmium cell is 1.2 volts. It holds this voltage well for most of the discharge cycle, only falling when most of the charge has been used. It holds the output voltage better than the equivalent zinc carbon primary types which have a steady fall over the life of the cell. Whilst a flat curve shows the advantage that the output voltage from the cell is very stable, it does mean that when the cell nears the end of its discharge cycle, the output voltage falls off rapidly, often giving little warning to the user.

NiCd cells have a very low level of internal resistance. A good quality alkaline cell might have an internal resistance of about 300 milli-ohms when new. This figure might rise to about 900 milli-ohms when 20% discharged and several ohms when almost completely discharged. A NiCd has very much lower figures, and any internal resistance can be ignored for most purposes as it is of the order of only a few milli-ohms, dependent upon the exact type of cell and the manufacturer. This does mean that the cell is capable of producing very high currents, especially if the cell is accidentally short-circuited. In view of this care must be taken to ensure this does not happen as large amounts of heat can be generated.

NiCd construction

Nickel cadmium, NiCd cells consist of four main elements:

  • Anode:   This comprises a net that is cadmium plated.
  • Cathode:   The cathode electrode of the NiCd cell is a mesh that is nickel-plated.
  • Separator:   The separator is used to ensure that the anode and cathode do not physically touch and cause a short circuit.
  • Electrolyte:   The electrolyte serves to carry the ions and charge carriers between the anode and cathode. It can be either potassium hydroxide, KOH or Sodium Hydroxide. Of the tow potassium hydroxide conducts better, but sodium hydroxide does not leak as much.

In the discharged state the positive active material is consists of nickel hydroxide (Ni(OH)2 and the negative material is cadmium hydroxide. During charging these convert to NiO OH and cadmium together with some water. Although the separator does not take place in the reaction it serves to insulate between the plates. An electrolyte is also needed. Potassium hydroxide is used for this. It does not participate in the reaction, but enables electron transfer to take place between the two plates.

NiCd cell sizes

NiCd cells can be obtained in a variety of sizes, and often special NiCd battery packs may be manufactured for particular items of electronic equipment. However the most popular NiCd cells are those in the standard battery or cell sizes: AAA, AA, C, and D cells packages. These standard sizes for this are given below, although it has occasionally been found that some NiCds have exceeded these sizes making fitment to standard slots rather tight.

Cell type Diameter
AAA 10.5 44.5
AA 14.5 50.5
C 26.2 50.0
D 34.2 61.5

Precautions to ensure long life of NiCds

There are a number of precautions that can be observed to help extend the life of NiCd batteries. A short list is shown below:

  • Do not short circuit the cells as very large currents can be drawn. This can be dangerous as large amounts of heat can be generated. It is also advisable not to discharge the cells at very high rates.
  • Never overcharge the cells at a rate greater than or equal to their normal charging current. Trickle charging is permissible.
  • Never reverse charge the cells. This can occur when a battery consisting of several cells in series is completely discharged. As some cells will hold less charge than the rest, as the total battery becomes discharged, some cells will be put into the reverse charge situation.
  • Never discard cells in a fire.
  • Cells operate best under normal room temperature conditions. High and low temperatures reduce their effectiveness. High temperatures can cause permanent damage to the cell.

Nicd or NiCad cells batteries have been available for many years. Their use has all but finished in view of the environmental issues associated with their disposal. However some years ago, many NiCd batteries were available and tey were effectively the only form of rechargeable cell or battery for electronic equipment.